Prepainted 55% Aluminum-Zinc alloy coating steel sheet (SuperGalum) with a variety of coating options is available to meet the needs of our customers.
Ultra corrosion resistance of aluminum, as well as the sacrificial anodes of zinc are ideally combined to create a highly corrosion resistant prepainted steel sheet which is 3~6 times more durable than conventional hot-dip coated steel sheet.
Durability
Offers three to six times greater durability compared with galvanized steel sheet coated at the same thickness
Cost efficiency
The density of a 55% Al-Zn coating layer is lower than that of zinc coating, increasing the surface per ton by approximately 1~3%
Superb paintability
Adhesiveness between the coating layer and paint is superior to galvanized steel plates.
Excellent workability
The level of workability is identical to that of galvanized steel sheet. Due to its ability to prevent fine cracks from developing, durability of the treated portion is also high. |
|
|
|
|
|
|
USAGE |
|
- -Sandwich panel
- -Roof panel
- -Coastal factory complex
|
|
DESCRIPTION |
|
Cross section of painted product
the Composition
Composition |
Weight Ratio (%) |
Capacity Ratio (%) |
Aluminum |
55.0 |
80 |
Zinc |
43.4 |
19 |
Silicon |
1.6 |
1 |
Size availability
Test items
Polyester
the TEST Polyester
Test item |
Test method |
Test result |
Related specification |
Cross cut test |
100 × 100 TAPING TEST
|
Good |
KS D 3520 |
Pencil Hardness test |
45˚, 1H and over |
Good |
KS D 3520 |
Bending test |
180˚×3T |
Good |
KS D 3520 |
Impact test |
500g×12.7㎜φ×500㎜H |
Good |
KS D 3520 |
Salt water spray test |
5%Nacl 35˚ |
500hours Good |
KS D 9520 JIS Z 2371 |
Resistance to Chemicals |
5%H₂SO₄×5Hr 5%NaOH×5Hr |
Good Good |
DS-B-I-1112 |
Accelerated weathering test |
Weather-O-Meter |
750hours Good |
JIS Z 0230 |
Film Hardness test |
M.E.K Rubbing |
40Times Good |
DS-B-I-1112 |
Silicon
TEST Silicon
Test item |
Test method |
Test result |
Related specification |
Cross cut test |
11×11-㎜ |
Good |
KS D 3520 |
Pencil Hardness test |
45˚, 1H and over |
Good |
KS D 3520 |
Bending test |
180˚×3T |
Good |
KS D 3520 |
Impact test |
500g×12.7㎜φ×500㎜H |
Good |
KS D 3520 |
Salt water spray test |
5%Nacl 35˚ |
750hours Good |
KS D 9520 JIS Z 2371 |
Resistance to Chemicals |
5%H₂SO₄×5Hr 5%NaOH×5Hr |
Good Good |
DS-B-I-1112 |
Accelerated weathering test |
Weather-O-Meter |
1300hours Good |
JIS Z 0230 |
Film Hardness test |
M.E.K Rubbing |
40Times Good |
DS-B-I-1112 |
SUN CLEAN
the TEST SUN CLEAN
Test item |
Test method |
Test result |
Related specification |
Cross cut test |
11×11-㎜ |
Good |
KS D 3520 |
Pencil Hardness test |
45˚, 1H and over |
Good |
KS D 3520 |
Bending test |
180˚×3T |
Good |
KS D 3520 |
Impact test |
500g×12.7㎜φ×500㎜H |
Good |
KS D 3520 |
Salt water spray test |
5%Nacl 35˚ |
750hours Good |
KS D 9520 JIS Z 2371 |
Resistance to Chemicals |
5%H₂SO₄×5Hr 5%NaOH×5Hr |
Good Good |
DS-B-I-1112 |
Accelerated weathering test |
Weather-O-Meter |
750hours Good |
JIS Z 0230 |
Film Hardness test |
M.E.K Rubbing |
80Times Good |
DS-B-I-1112 |
SUN TEK
the TEST SUN TEK
Test item |
Test method |
Test result |
Related specification |
Cross cut test |
11×11-㎜ |
Good |
KS D 3520 |
Pencil Hardness test |
45˚, 1H and over |
Good |
KS D 3520 |
Bending test |
180˚×3T |
Good |
KS D 3520 |
Impact test |
500g×12.7㎜φ×500㎜H |
Good |
KS D 3520 |
Salt water spray test |
5%Nacl 35˚ |
500hours Good |
KS D 9520 JIS Z 2371 |
Resistance to Chemicals |
5%H₂SO₄×5Hr 5%NaOH×5Hr |
Good Good |
DS-B-I-1112 |
Accelerated weathering test |
Weather-O-Meter |
1000hours Good |
JIS Z 0230 |
Film Hardness test |
M.E.K Rubbing |
40Times Good |
DS-B-I-1112 |
|
|